AT6001 100g Adhesives and Sealants

Adhesive;Optical Waveguide;Acrylate;10g

Adhesive;Optical Waveguide;Acrylate;500g

Viscosity 70->20,000 mPas; Shear Bond Strength > 69->200 kgf/cm²; Bending Adhesion Strength 9-25 kgf/cm²; UV Curing Conditions 10-100 mW/cm², 5, 10 min; Colour Light Yellow, Colourless, White; Tg +42-+219 °C NTT-AT’s series of adhesives for fiber array assemblies feature high moisture resistance and excellent workability for v-groove fixing or optical fiber fixing. Fiber arrays are used for the input and output of optical waveguide devices. NTT-AT’s AT3925M, AT9390, AT9968, AT3727E and AT3728E epoxy-based optical adhesives are used for fixing the v-grooves and have realized price reductions while enhancing moisture resistance compared to conventional products. These adhesives can be polished after assembly. NTT-AT’s AT9575M (epoxy) and AT8105 (acrylate) adhesives for optical fiber fixing have gained popularity for their good workability as non-fluid adhesives. NTT-AT has executed durability tests that have shown no peeling of a fiber array after 2,000 hours at +85 °C and 85% of humidity. With viscosities that are appropriate for the usage location, the adhesives for fiber array assemblies are easy to use. While the adhesives for fixing v-grooves show fluidity, the optical fiber fixing adhesives’ consistency is that of a paste, suitable for protecting the fiber. In case you need any consulting regarding issues related to adhesion, please contact the AMS Technologies optical adhesives experts to discuss the detailed challenges of your application. Key Features: Excellent Durability Just the Right Viscosity for Easy Application: Non-liquid Viscosity for Fiber Fixation, Low Viscosity Fluid for Fiber Fixation into V-Type Groove Heat-proof: Maximum Glass Transition Temperature Tg of Over +200 °C (AT3925M) Viscosity: 70 to >20,000 mPas Shear Bond Strength: > 69 to >200 kgf/cm² Bending Adhesion Strength: 9 to 25 kgf/cm² UV Curing Conditions: 10 to 100 mW/cm², 5, 10 min Colour (Pre-Curing): Light Yellow, Colourless, White Glass Transition Temperature Tg: +42 to +219 °C Applications: Gluing of Fiber Array Assemblies; V-Groove Fixing; Optical Fiber Fixing

Adhesive;Optical Waveguide;Acrylate;200g

Adhesive;Optical Waveguide;Acrylate;5g

Adhesive;Optical Waveguide;Acrylate;300g

Refractive Index 1.458-1.567; Viscosity 145-2,000 mPas; Optical Transmittance (@1 mm, 1.3 µm) 82%-94%; Bond Strength 99->247 kgf/cm²; UV Curing Conditions 10, 30 mW/cm², 5, 10 min You are looking for PLC and fiber array adhesion with high reliability? Try NTT-AT’s series of adhesives for optical waveguides! Within this series you find acrylate-based adhesives (AT6001, AT8224)with excellent durability that have cleared a large number of reliability tests. Epoxy adhesives are also part of this series, with a refractive index that can be accurately controlled within a range of 1.456 to 1.567 (±0.005, Na-D) – or with a fixed refractive index that is the same as quartz to deliver low reflectance (GA700L, GA700H). UV curing of the adhesives for optical waveguides allows for adhesion in a short time frame and makes alignment easy. The adhesives withstand a solder reflow process for Si Photonics (+260 °C). In order to achieve high reliability, a product must clear the tests conducted by the users themselves. If you have had even just a bit of dissatisfaction in reliability test results in the past, please put NTT-AT’s adhesives for optical waveguides to the test. In case you need any consulting regarding issues related to adhesion, please contact the AMS Technologies optical adhesives experts to discuss the detailed challenges of your application. Key Features: Optical Adhesive Used for PLC to Fiber Link-up Precision Refraction Index of 1.458 to 1.567 (±0.005, Na-D) Provides Controllability Ultraviolet (UV) Curing Conditions: 10, 30 mW/cm², 5, 10 min Very Little Adhesion Loss Due to Heat or Moisture, Providing High Durability Viscosity: 145 to 2,000 mPas Optical Transmittance: 82% to 94% (@1 mm Thickness, Wavelength 1.3 µm) Bond Strength: 99 to >247 kgf/cm² Applications: Gluing of Optical Waveguides; PLC to Fiber Link-up; Silicon Waveguide to Fiber Link-up